Gallium
Gallium X-ray photoelectron spectra, gallium electron configuration, and other elemental information.
Join the conversation
Gallium • Other Metal
Primary XPS region: Ga2p, Ga3d
Overlapping regions: In4d, O2s
Binding energies of common chemical states:
| Chemical state | Binding energy Ga2p3/2 | Binding energy Ga3d5/2 |
|---|---|---|
| Ga elemental | 1116.7 eV | 18.7 eV |
| GaAs | 1116.9 eV | 19.1 eV |
| Ga2O3 | 1118.0 eV | 20.5 eV |
| GaAs native oxide | 1117.8 eV | 20.3 eV |
| Ga native oxide | 1118.7 eV | 20.9 eV |
Experimental information
- Possibility of elemental gallium melting during prolonged X-ray analysis.
- Ga2p or Ga3d typically used.
- Using the Ga2p peak will give better depth resolution for sputter profiling.
- Ga3d electrons have higher kinetic energy and therefore have a deeper sampling depth compared to the low kinetic energy Ga2p electrons.
- The Ga3d region is sometimes more informative for chemical analysis.
- Using the Ga2p peak will give better depth resolution for sputter profiling.
Interpretation of XPS spectra
- Ga2p region has significantly split spin-orbit components (Δ=26.9eV, intensity ratio=0.491).
- Ga2p peaks have asymmetric lineshape for elemental gallium and symmetric lineshapes for compounds.
- Typically only the Ga2p3/2 component of the Ga2p region is fitted and quantified.
- Loss feature may be observed between spin-orbit components (1130eV).
General comments
- Ga LMM peaks (between 400eV-600eV) overlap with many XPS peaks from other elements.
- Ga3d peak has overlapping spin-orbit components (Δ=0.46eV, intensity ratio=0.633).
- Splitting is observable for elemental gallium, but may be ignored for gallium compounds.
- Ga3d overlaps strongly with In4d (17eV) and O2s (23.5eV) regions.
- Ga3d peaks have asymmetric lineshape for elemental gallium and symmetric lineshapes for compounds.
About this element
Symbol: Ga
Date of discovery: 1875
Name origin: Latin Gallia
Appearance: white/silver
Discoverer: Paul Emile Lecoq de Boisbaudran
Obtained from: bauxite, germanite, coal
Melting point: 29.87 K
Boiling point: 2204 K
Density[kg/m3]: 5.907
Molar volume: 11.80 × 10-6 m3/mol
Protons/Electrons: 31
Neutrons: 39
Shell structure: 2,8,18,3
Electron configuration: [Ar]3d104s24p1
Oxidation state: 3,1
Crystal structure: Orthorhombic
Very pure gallium metal has a brilliant silvery color. In its solid state, this metal fractures like glass. Due to its very low melting point, it is possible to melt gallium in one’s hand, although this is not recommended. When storing this element, special considerations must be taken into account. The metal expands when it solidifies, making glass storage difficult. It also attacks most other metals by diffusing into their metal lattice making storage in steel or aluminum containers impossible. Since gallium wets glass and porcelain, it can be used to create brilliant mirrors. Gallium nitrate has even been used in the treatment of arthritis.
Products
Style Sheet for Instrument Cards Original
Style Sheet for Global Design System
Style Sheet for Komodo Tabs
Style Sheet to change H3 to p with em-h3-header class
Style Sheet to change H2 style to p with em-h2-header class
Style Sheet for Products Table Specifications
Style Sheet for Global Design System
Style Sheet for Komodo Tabs
Style Sheet to change H3 to p with em-h3-header class
Style Sheet to change H2 style to p with em-h2-header class
Style Sheet for Products Table Specifications
Fix for left nav
Style Sheet for Support and Service footer
Style Sheet for Fonts
Style Sheet for Cards
Electron microscopy services for
the materials science
To ensure optimal system performance, we provide you access to a world-class network of field service experts, technical support, and certified spare parts.